ZATEZNA SVOJSTVA ČISTOG PLA POLIMERA ZA ADITIVNU PROIZVODNJU

Aleksa Milovanović1*, Aleksandar Sedmak2, Milovan Paunić2, Aleksandra Mitrović3,4, Mihajlo Popović2, Miloš Milošević1

1) Innovation Centre of the Faculty of Mechanical Eng., Belgrade, SERBIA

A. Milovanović 0000-0003-4668-8800; M. Milošević 0000-0002-2418-1032, *email: amilovanovic@mas.bg.ac.rs

2) University of Belgrade, Faculty of Mechanical Engineering, Belgrade, SERBIA

A. Sedmak 0000-0002-5438-1895; M. Paunić 0000-0002-4180-9813; M. Popović 0000-0003-3607-9243

3) University Union-Nikola Tesla, Faculty of Information Technology and Engineering, Belgrade, SERBIA

A. Mitrović 0000-0002-5183-6276

4) The Academy of Applied Technical Studies, Belgrade, SERBIA

 

Izvod

Cilj istraživanja je pružanje celovite slike o zateznim svojstvima materijala na osnovu eksperimenata na uzorcima sa 100 % ispunom (za 0.3; 0.2; 0.1 mm visine sloja) i sve ostale količine ispune (od 90 do 10 %, sa inkrementom 10 %), dobijeno interpolacijom rezultata iz prethodnih istraživanja. Zatezanje je rađeno prema ISO 527-2 standardu. Zatim se sa MKE analizira 100 % ispuna, radi verifikacije MKE modela. Time je pokazano da korišćeni konstitutivni modeli ovog termoplastičnog materijala i same MKE simulacije odgovaraju eksperimentalnim podacima.

Ključne reči: aditivna proizvodnja, modeliranje deponovanjem topljenog materijala, PLA, zatezna svojstva, MKE analiza  