UDARNA ŽILAVOST ZAVARENIH SPOJEVA ČELIKA SIMAXX 1000

Snežana Joksić1 , Ivica Čamagić1 , Aleksandar Sedmak2 , Bojan Medjo3 ,

Zijah Burzić4 , Shengwen Tu5 , Stefan Dikić3

1) University of Kosovska Mitrovica, Faculty of Technical Sciences, SERBIA

S. Joksić https://orcid.org/0009-0002-1909-2462 ; I. Čamagić https://orcid.org/0000-0003-4706-6333

2) University of Belgrade, Faculty of Mechanical Engineering, Belgrade, SERBIA

A. Sedmak https://orcid.org/0000-0002-5438-1895 , *email: asedmak@mas.bg.ac.rs

3) University of Belgrade, Faculty of Technology and Metallurgy, Belgrade, SERBIA

B. Medjo https://orcid.org/0000-0001-8100-7519 ; S. Dikić https://orcid.org/0000-0003-2700-0628

4) Society for Structural Integrity and Life ‘Prof. dr Stojan Sedmak’, Belgrade, SERBIA

Z. Burzić https://orcid.org/0000-0002-4759-9853

5) School of Chemical Engineering and Technology, Xi'an Jiaotong University, CHINA

S. Tu https://orcid.org/0000-0001-8735-5661

 

Izvod

Analizirano je ponašanje zavarenih spojeva niskolegiranog čelika ultra visoke jačine, SIMAXX 1000, pri lomu usled udarnog opterećenja. Za udarno ispitivanje je korišćeno instrumentirano Šarpijevo klatno, u cilju razdvajanja ukupne energije na energije nastajanja i rasta prsline. Korišćene su standardne epruvete sa zarezom u osnovnom metalu (OM), zoni uticaja toplote (ZUT) i u metalu šava (MŠ), kako bi se utvrdio uticaj heterogene mikrostrukture zavarenog spoja. Uticaj niske temperature do –60 °C je takođe analiziran, kako bi se potvrdilo da je čelik SIMAXX 1000 upotrebljiv i na niskim temperaturama. U tom cilju je određena temperatura prelaska u krti lom.

Ključne reči: • SIMAXX 1000 • udarna žilavost • zone zavarenog spoja • temperatura prelaska u krti lom