UPOREDNA TRIBOLOŠKA ANALIZA LEGURA TIPA Al-Fe-Si I Al-Fe-Cr

Haidar Faisal Helal Mobark1, Ali Hussein Al-Azzawi2, Abdulraheem Kadhim AbidAli3, Barhm Mohamad4*

1) College of Agriculture, Al-Qasim Green University, Babel, IRAQ

H.F.H. Mobark  0000-0001-6809-8452

2) Department of Mechanical Engineering, College of Engineering, University of Misan, Misan, IRAQ

A.H. Al-Azzawi  0000-0003-4402-6205

3) College of Materials Engineering, University of Babylon, Babel, IRAQ

A.K. AbidAli  0000-0001-8961-0339

4) Department of Petroleum Technology, Koya Technical Institute, Erbil Polytechnic University, Erbil, IRAQ

B. Mohamad  0000-0001-8107-6127  *email: barhm.mohamad@epu.edu.iq

 

Izvod

U ovom radu je predstavljeno uporedno istraživanje tribološkog ponašanja i mikrostrukturnih karakteristika dve različite legure, zapravo, 77,3 % Al-1,8 % Fe-16,7 % Si i 54,1 % Al-12,8 % Fe-27,8 % Cr. Visokotemperaturne legure se proizvode metodom vrtložnog livenja. Tribološka analiza se izvodi za procenu trošenja, formiranja prslina, i šupljih zona za obe legure, primenom skening elektronske mikroskopije (SEM). Pored toga, optička mikrografija se primenjuje za analizu mikrostruktura. Rezultati pokazuju značajne razlike između ovih legura, gde 77,3 % Al-1,8 % Fe-16,7 % Si legura pokazuje veću Vikers tvrdoću i izuzetnu otpornost na habanje u poređenju sa legurom 54,1 % Al-12,8 % Fe-27,8 % Cr. Optički mikrosnimci potvrđuju dobro definisanu raspodelu zrna u prvoj leguri, kao i sličnu homogenu mikrostrukturu kod druge legure.

Ključne reči: nauka o materijalima, vrtložno livenje, proizvodnja legura, tribološka analiza, površinsko oštećenje