MIKROSTRUKTURA, MIKROTVRDOĆA I HEMIJSKI SASTAV DELA SKLOPA U IZVOĐENJU ELEKTROLUČNIM NAVARIVANJEM NA HARDVER-SOFTVER KOMPLEKSU TIPA DELTA

Maxim A. Kuznetsov1, Andrei V. Proskokov1, Dmitry P. Il’yaschenko1,2*, Elena V. Lavrova3

1) National Research Tomsk Polytechnic University, Tomsk, RUSSIAN FEDERATION

M.A. Kuznetsov  0000-0003-3919-3009; A.V. Proskokov  0000-0003-3526-4674;

D.P. Il’yaschenko  0000-0003-0409-8386   *email: mita8@rambler.ru 

2) Institute of Strength Physics and Materials Science of Siberian Branch Russian Academy of Sciences, Tomsk, RUSSIAN FEDERATION

3) Pryazovskyi State Technical University, Mariupol, RUSSIAN FEDERATION

E.V. Lavrova  0000-0001-6030-0986

 

Izvod

U radu se izvodi elektrolučno navarivanje sloj-po-sloj niskougljeničnom niskolegiranom žicom u zaštiti ugljen-dioksidom. Naneta struktura metala, oblika paralelopipeda debljine 4 mm i visine 40 mm, je poslužila za određivanje mikrostrukture optičkom mikroskopijom, sastava mikrotvrdoćom utiskivanjem i hemijskog sastava metodom spektralne analize emisije atoma. Dobijeni rezultati pokazuju da dobijeni proizvodi imaju gradijentnu strukturu. Samo je poslednji sloj imao dendritnu strukturu. Prethodni slojevi, dvostruko termički obrađeni, usled oslobađanja toplote gornjeg sloja, imaju poliedarsku rekristalizovanu finozrnu feritno-perlitnu strukturu. Mikrotvrdoća izbačenih nanetih vlakana se menja od 1760 MPa do 1360 MPa u gornjim nanetim slojevima. Ovo je istovremeno i opšti pad frakcije perlita i po definiciji ferit. Određivanje hemijskog sastava nanetog metala pokazuje da u prvom-četvrtom slučaju, dolazi do promena u metalu navarene žice i u metalu supstrata, kao i u procentu hemijskih elemenata po debljini sa šestim sastavom od dvadeset približno uslovljava metal žice za navarivanje.

Ključne reči: elektrolučno navarivanje metalnom žicom, mikrostruktura, mikrotvrdoća, hemijski sastav