Vol.25, No.3, 2025, pp. 487–494
https://doi.org/10.69644/ivk-2025-03-0487  

ANALIZA TERMIČKIH I ZAOSTALIH NAPONA U VIŠESLOJNO ZAVARENIM CEVIMA OD NERĐAJUĆEG ČELIKA KORIŠĆENJEM DEFLUX I FILM POTPROGRAMA

Abdelhakim Amine Djendara1 , Mohamed El Amine Khiari2* , Abdallah Benzaama2

1) University of Science and Technology of Oran-Mohamed Boudiaf (USTO-MB), AlLGERIA

A.A. Djendara https://orcid.org/0009-0001-5736-306X

2) National Polytechnic School of Oran-Maurice Audin, ALGERIA

M. El Amine Khiari https://orcid.org/0009-0009-9379-2038 , *email: mohamedelamine.khiari@gmail.com ;

A. Benzaama https://orcid.org/0000-0002-3564-6157 

 

Izvod

Ovaj rad daje sveobuhvatnu analizu uticaja parametara zavarivanja, konkretno brzine zavarivanja i broja prolaza, na raspodelu zaostalih napona u cevima od austenitnog nerđajućeg čelika AISI 304 (Z7CN18-09). Razvijen je trodimenzionalni model metode konačnih elemenata (FEM) u ABAQUS®-u za simulaciju procesa cirkularnog zavarivanja. Potprogrami DFLUX i FILM korišćeni su za predstavljanje dvostrukog elipsoidnog pokretnog izvora toplote i termičkih graničnih uslova. Validacija modela izvršena je upoređivanjem simuliranih profila šavova i termičkih ciklusa sa eksperimentalnim podacima, što pokazuje izuzetno poklapanje (devijacija < 5 %).

Spregnuta termičko-mehanička analiza omogućuje procenu prostorno-vremenskog razvoja temperaturnog polja pri različitim brzinama zavarivanja (80, 160 i 240 mm/min) i raspodelu aksijalnih i cirkularnih zaostalih napona po debljini cevi. Numerički rezultati ističu značajan uticaj parametara zavarivanja na veličinu i raspodelu zaostalih napona. Optimizovane brzine zavarivanja pokazuju smanjenje maksimalnih nivoa napona, dok višeprolazno zavarivanje poboljšava ujednačavanje napona.

Ključne reči: • AISI 304 nerđajući čelik • zaostali naponi • metoda konačnih elemenata (FEM) • višeslojno zavarivanje • prenos toplote