UDARNA SVOJSTVA FDM PLA POLIMERA U ODNOSU NA KOLIČINU ISPUNE

Aleksa Milovanović1* , Milovan Paunić2 , Sergiu-Valentin Galațanu3 , Ivana Filipović1 , Miloš Milošević1 , Liviu Marșavina3 , Aleksandar Sedmak2

1) University of Belgrade, Innovation Centre of the Faculty of Mechanical Engineering, Belgrade, SERBIA

A. Milovanović https://orcid.org/0000-0003-4668-8800 , *email: aleksa753@gmail.com , amilovanovic@mas.bg.ac.rs

I. Filipović https://orcid.org/0000-0002-7977-2980 ; M. Milošević https://orcid.org/0000-0002-2418-1032

2) University of Belgrade, Faculty of Mechanical Engineering, Belgrade, SERBIA

M. Paunić https://orcid.org/0000-0002-4180-9813 ; A. Sedmak https://orcid.org/0000-0002-5438-1895

3) Department of Mechanics and Strength of Materials, Politehnica University of Timisoara, Timișoara, ROMANIA

S.-V. Galațanu https://orcid.org/0000-0002-7629-8662 ; L. Marșavina https://orcid.org/0000-0002-5924-0821

 

Izvod

Fokus ovog istraživanja je na proceni uticaja količine ispune na udarna svojstva PLA materijala za FDM upotrebu, odnosno, kako udarna svojstva degradiraju sa manjim ispunama. Većina FDM uređaja mogu da naprave delove sa 10 % do 100 % količine ispune. Ovde uzimamo u obzir ceo spektar ispuna sa inkrementom od 10 % (ukupno 10 grupa uzoraka). Prethodna istraživanja autora su pokazala prednosti manjih visina sloja u pogledu ponovljivosti rezultata i vrednosti udarne žilavosti. Stoga, ovde koristimo 0.1 mm za visinu sloja, najmanju za većinu FDM uređaja. Ispitivanja su izvršena na sobnoj temperaturi i pri kontrolisanoj vlažnosti od oko 50 % na Šarpi instrumentiranom klatnu.

Ključne reči: • PLA • modeliranje deponovanjem topljenog materijala • količina ispune • udarno ispitivanje po Šarpiju • instrumentalizovano klatno 